32% Glass Fiber Reinforced Polycarbonate
1011582CT PC E-14961B GF32 BLKBLK
Description
Availability
North America
Legend
SDS - Safety Data Sheet
PSB - Product Stewardship Bulletin
Product Data and Technical Information
| Melt Flow Rate (300 °C/1.2 kg) | 5.4 g/10 min |
| Melt Flow Rate (300 °C/3.8 kg) | 27 g/10 min |
| Melt Flow Rate (300 °C/5.0 kg) | 30 g/10 min |
| Density - Specific Gravity | 1.43 g/cm³ |
| Flexural Strength at Yield (1.3 mm/min) | 118 MPa |
| Tensile Strength at Break (5.0 mm/min, 23 °C, 3.11 mm, Injection Molded) | 117 MPa |
| Flexural Modulus (1.3 mm/min, 1% Secant) | 7790 MPa |
| Tensile Elongation at Break (5.0 mm/min, 23 °C, 3.11 mm, Injection Molded) | 2.7 % |
| Tensile Modulus (5.0 mm/min, 23 °C, 3.11 mm, Injection Molded) | 440 MPa |
| Unnotched Izod Impact (23 °C, 3.08 mm) | 930 J/m |
| Notched Izod Impact (23 °C, 3.07 mm) | 180 J/m |
| Deflection Temperature Under Load Unannealed (264 psi) (12.6 mm) | 142 °C |
| Deflection Temperature Under Load Unannealed (66 psi) (12.6 mm) | 146 °C |
| Coefficent of Linear Thermal Expansion (CLTE), Flow (-20 to 130 °C) | 1.8E-5 cm/cm/°C |
| Coefficent of Linear Thermal Expansion (CLTE), Perpendicular (-20 to 130 °C) | 6.5E-5 cm/cm/°C |
| Burning Rate (2.00 mm) | <100 mm/min |
| Burning Rate (2.00 mm) | <100 mm/min |
| Drying Time | 3.0 to 6.0 hr |
| Nozzle Temperature | 304 to 338 °C |
| Drying Temperature | 121 °C |
| Front Temperature | 304 to 338 °C |
| Processing (Melt) Temp | 316 to 343 °C |
| Mold Temperature | 82 to 116 °C |
| Middle Temperature | 293 to 316 °C |
| Rear Temperature | 282 to 304 °C |
| Drying Time, Maximum | 6 hr |
Technical Data Sheet
Technical Data Sheet - APS InjectionProcess
Extrusion, Injection Molding
Resin
Polycarbonate