Pro-fax SG702 high impact polypropylene copolymer is available in pellet form. This resin is typically used in injection molding applications and offers very good cold temperature impact resistance.
ASTM and ISO-based versions of the technical data sheet are available for Pro-fax SG702.
Pro-fax SG702
Description
Availability
North America
Legend
SDS - Safety Data Sheet
PSB - Product Stewardship Bulletin
Product Data and Technical Information
| Melt Flow Rate (230 °C/2.16 kg) | 18 g/10 min |
| Density (23 °C) | 0.90 g/cm³ |
| Density (23 °C, Method A) | 0.90 g/cm³ |
| Flexural Modulus (23 °C) | 970 MPa |
| Flexural Modulus (0.05 in/min, 1% Secant, Procedure A) | 150000 psi |
| Flexural Modulus (1.3 mm/min, 1% Secant, Procedure A) | 1030 MPa |
| Tensile Strength at Yield (2 in/min) | 3000 psi |
| Tensile Strength at Yield (50 mm/min) | 20 MPa |
| Tensile Stress at Yield (23 °C) | 20 MPa |
| Tensile Elongation at Yield | 6 % |
| Tensile Strain at Yield (23 °C) | 6 % |
| Charpy Impact Strength - Notched (23 °C) | 16 kJ/m² |
| Charpy Impact Strength - Notched (-40 °C) | 2.6 kJ/m² |
| Notched Izod Impact Strength (23 °C) | 42 kJ/m² |
| Notched Izod Impact Strength (-40 °C) | 5.0 kJ/m² |
| Notched Izod Impact Strength (73 °F, Method A) | No Break ft-lb/in |
| Notched Izod Impact Strength (23 °C, Method A) | No Break J/m |
| Deflection Temperature Under Load (66 psi, Unannealed) | 183 °F |
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 71 °C |
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 84 °C |
| Deflection Temperature Under Load (1.80 MPa, Unannealed) | 49 °C |
| Mold Shrinkage |
Process
Compounding, Injection Molding
Resin
Polypropylene, Impact Copolymer
Applications
Automotive Parts, Containers, Sports, Leisure & Toys